레이저 분말 베드 용융법으로 제작된 Hastelloy X 적층 소재의 시편 두께 및 서포트 구조에 따른 잔류응력 변화

초록

The purpose of this study was to investigate the effects of sample thickness and support structure on the residual stress of Hastelloy X superalloy samples fabricated by laser powder bed fusion (LPBF), which is an additive manufacturing process. The residual stresses of LPBF samples with different thicknesses and support structures were measured using X-ray diffraction. The results revealed that as the thickness of sample increased from 2.5 mm to 20 mm, its tensile residual stress gradually decreased from 443.5 MPa to 182.2 MPa. Additionally, the residual stress in the bottom region of sample was higher than that in the top region, and the residual stress difference in the bottom and top regions became more pronounced as the sample thickness decreased. The residual stress of LPBF sample also varied depending on the structure of support. The residual stress of sample decreased with increasing contract area between the sample and the support, because the larger contract area led to smaller temperature gradient throughout the sample.

키워드