Diffusion bonding at the interface of Bi2Te3 thermoelectric modules

초록

In production of Bi2Te3-based thermoelectric modules, Bi2Te3 materials were coated with electroless nickel (EN), electroless palladium, and immersion gold multilayers to suppress unanticipated interfacial reactions between Bi2Te3 and Sn-based solder alloys. However, the coating elements reacted with the solder alloys to yield intermetallic compounds (IMCs) at the Bi2Te3/solder and solder/Cu electrode interfaces. Significant Cu content from the Cu electrodes contributed to the IMCs along with to the coating and Sn elements. In this study, the influence of IMC composition on bonding strength and the characteristics of the Bi2Te3-based material/Cu electrode interface was investigated. An EN layer was plated onto Cu electrodes to suppress Cu diffusion from the electrodes into the solder alloy. IMCs mainly consisted of Sn and Cu elements in the case of uncoated Cu electrodes. When Cu electrodes were coated by the EN layer, Ni and Sn content prevailed in IMC composition. Additionally, IMCs at both the Bi2Te3/solder and solder/Cu electrode interfaces with Cu or Pd were thicker than those without Cu or Pd. Meanwhile, the bonding strength of the Bi2Te3-based material/Cu electrode interface with the EN layer on the Cu electrodes was lower than that of the interfaces without the EN layer.

키워드