The Mechanistic Determination of Doping Contrast from Fermi Level Pinned Surfaces in the Scanning Electron Microscope Using Energy-Filtered Imaging and Calculated Potential Distributions

초록

Secondary electron (SE) doping contrast in the scanning electron microscope is correlated with Fermi level pinned surfaces of Si samples prepared using HF-based wet-chemical treatment or focused ion beam (FIB) micromachining en route to quantitative dopant profiling. Using energy-resolved SE imaging techniques and finite-element analyses of surface states and surface junction potentials, we clarified the surface band-bending effects post-NH4F-treatment, consistent with brighter p-contrast from degenerately doped (>10(19) cm(-3)) regions. In general, SE spectromicroscopy scan measurements unambiguously indicated heavy suppression of patch fields, while the empirical discovery of scan frequency-modulated contrast inversion due to Chee et al. [Springer Proceedings in Physics, 120, pp. 407-410 (2008)] is ascribable to competing fixed oxide charge and dynamic charge injection phenomena ( particularly at dwell times >29 mu s). Leveraging numerical simulations of electric potentials and variable-voltage experimental data, the theoretical model based on amorphization damage-mediated Fermi level pinning is elucidated for Ga+ FIB-processed site-specific doping contrast on patch field-free surfaces. This work successfully argues against the notion that doping contrast ultimately or exclusively entails patch fields or adventitious metal-semiconductor contacts.

키워드