Crystal growth, luminescence, and scintillation properties of Zn2Te3O8 crystal for 0νββ decay search

초록

A single crystal of Zn2Te3O8 (ZTO) was grown using the conventional Czochralski technique. TGA analysis showed that the melting point of ZTO is 681 degrees C, while it exhibits a structural phase transition at 621 degrees C. The powder X-ray diffraction analysis of ZTO confirmed that it possesses a single crystalline monoclinic structure with the C2/c space group. An indirect band gap of 3.75 eV was estimated for the ZTO crystal based on its absorption spectrum. The X-ray-induced luminescence of the grown crystal comprised a broad band peaking at 565 nm, which can be tentatively assigned to the self-trapped exciton emission from the (Te3O8)(4-) molecular complexes. The photoluminescence measured under 280 nm excitation showed a broad band luminescence peaking at about 600 nm, and its intensity was significantly enhanced upon cooling the crystal from 300 K to 10 K. The photoluminescence decay time under 280 nm excitation was shown to have two exponential components in the range from 10 K to 175 K, which became a single exponential upon further heating the crystal. Low scintillation light was observed at room temperature both under alpha- and beta-particle excitations from Am-241 and Sr-90 sources, respectively. The scintillation light yield measured under beta-particle excitation from the Sr-90 source was enhanced by about five orders of magnitude at 10 K in comparison to that at 300 K. The scintillation light yield measured at 10 K under the same experimental conditions for ZTO in comparison with the well-known cryogenic scintillator Li2MoO4 (LMO) was shown to have four times higher scintillation light. A single-crystal ingot of ZTO was obtained for the first time; however, it had several cracks due to its phase transition. Notably, scintillation at low temperatures for a Te-based crystal was observed for the first time. These preliminary findings are very promising and show that ZTO will be a good candidate for cryogenic phonon scintillation detectors for the 0 nu beta beta decay search of Te-130.

키워드